ings' target='_blank'>casting dimension precision is influenced by structure of casting, casting material, moulding, shell making, roasting, pouring the influence of various factors, such as any one link set, unreasonable operation can make the casting shrinkage rate of change, has led to the deviation of dimension accuracy of castings and requirements.
1, the influence of the casting structure: a, casting wall thickness, shrinkage rate is large, thin wall castings, the shrinkage rate is small.
B, free shrinkage, hinder the little shrinkage.
2, the influence of the casting material: a, the higher the carbon content in material, line the smaller shrinkage rate, the lower the carbon content, the line, the greater the shrinkage rate.
B, the common material casting shrinkage rate is as follows: casting shrinkage ratio K = (
100%, LM for cavity size, LJ for casting size.
K by the following factors: the wax models K1, K2, alloy casting structure types K3, K4 pouring temperature.
3, the influence of the molding shrinkage of casting line: a wax, wax temperature, pressure, the influence of the holding time of molten mould size to wax mould temperature, followed by wax mould pressure, pressure maintaining time after guarantee casting molding will have little impact on the casting size.
B, wax (
The line of shrinkage is about 0.
C, deposit moudle, will further produce contraction, the shrinkage value is about 10% of the total shrinkage, after 12 hours, but when stored moudle size basically stable.
D, wax models of radial shrinkage rate was only about shrinkage rate of 30 - the length direction
Shoot 40%, wax temperature effect on the free shrinkage rate is much greater than stuck to the influence of shrinkage,
Wax mould temperature for 57 -
59 ℃, the higher the temperature the greater the shrinkage)
4, the influence of the shell material: zircon sand, zircon powder, sand, powder, because of its small expansion coefficient, just 4.
6 / ℃, so can be neglected.
5, the influence of the type of shell roasting: due to the shell of the small expansion coefficient, when the shell temperature of 1150 ℃, is only 0.
As a result, 053%, and can be neglected.
6, the influence of pouring temperature, the higher the pouring temperature, the shrinkage rate, the greater the pouring temperature is low, the smaller the shrinkage rate, thus pouring temperature should be appropriate.
Xin er, the transportation is convenient in: guangzhou, high-speed, high-speed Shen Hai, same highways as well.
Is a company specializing in the production of cast copper, cast iron
, cast aluminum manufacturers.
Anyone who has seen the latest cast iron company cast iron suppliers
in operation cannot help but be impressed with how far the technology has progressed over the past few years.
Guangzhou Xinerxun Metal Trading Co., Ltd. is a professional manufacturer of offering some of the best in class cast iron suppliers solutions to global market. Click Xin Wilson Foundry to learn more.
We afford not only the best product but also the comprehensive service, satisfy the customer's demands.